The use of stainless steel pipes is now more and more extensive. Because of its good corrosion resistance, it plays a crucial role in engineering construction. In the process of production, we need to perform solution treatment on stainless steel pipes. The main purpose is to obtain certain Martensite increases the hardness of the product. Let's take a look at the solution treatment of stainless steel pipes:
(1) The intermediate aging method is heated to (760±15) degree after the solution treatment, and the temperature is kept for 90 minutes because Cr23C6 carbides are precipitated from the austenite, which reduces the carbon and alloying elements content in the austenitic 904L stainless steel pipe , the Ms point is raised to 70 degree and then cooled to room temperature to obtain martensite plus ferrite plus retained austenite structure, and the retained austenite is decomposed after aging at 510 degree .
(2) Pēc augstas temperatūras regulēšanas un kriogēnas apstrādes šķīdumu vispirms 90 minūtes karsē līdz 950 grādiem. Sakarā ar Ms punkta palielināšanos, atdzesējot līdz istabas temperatūrai, var iegūt nelielu daudzumu martensīta; martensīta daudzums.
(3) Pēc šķīduma apstrādes ar aukstās deformācijas metodi aukstā deformācija tiek veikta istabas temperatūrā. Martensīta daudzums, kas veidojas 904L bezšuvju caurulē aukstās deformācijas laikā, ir saistīts ar deformācijas apjomu un 904L nerūsējošā tērauda caurules sastāvu.
Iepriekš minētās trīs metodes parasti tiek izmantotas nerūsējošā tērauda cauruļu apstrādei ar šķīdumu. Es ceru, ka viņi var jums palīdzēt.